The advantage properties of aluminum alloy have light weight, excellent electrical and thermal conductivity, highly corrosion resistant and ductility.
Aluminum alloy is soft and are usually alloyed with copper, zinc, magnesium, silicon, manganese and lithium to increase strength. Aluminum alloy is exposed to air that instantly forms an anti-oxidant coating to protect products. Aluminum alloy is one of the lightest metals, the application of products ranges from precision technology to daily commodities.
Product Specification and Size :
Standard Specification: GB/T6892, ASTM B221, EN 755
| Alloy | Temper |
| 2xxx: 2007, 2011, 2024 | O, T3, T4, T3511 |
| 5xxx: 5083 | O, H112 |
| 6xxx: 6005, 6060, 6061, 6063, 6082, 6463 | O, H112, T5, T6, T66, T6511 |
Alloy designation (For Reference)
Comparison of Alloy Designations for Aluminum flat Products
| Alloy Series | Chinese Standard | American Standard | European Standard |
| 2xxx Series | 2024 | 2024 | EN AW-2024 |
| 5xxx Series | 5083 | 5083 | EN AW-5083 |
| 6xxx Series | 6005 | 6005 | |
| 6060 | 6060 | EN AW-6060 | |
| 6061 | 6061 | EN AW-6061 | |
| 6063 | 6063 | EN AW-6063 | |
| 6082 | 6082 | EN AW-6082 | |
| 6463 | 6463 |
Temper designation (For Reference)
| Temper | Definition |
| O | Annealed |
| H112 | Slightly strain harden from working at an elevated temperature or from limited amount of cold work |
| T3 | Solution heat-treated, cold worked and naturally aged |
| T3511 | Solution heat-treated, stress relived by stretching a controlled amount (permanent set 1% to 3% for extruded rod, bar, shapes and tube, 0.5% to 3% for drawn tube) and naturally aged |
| T4 | Solution heat-treated and naturally aged |
| T5 | Cooled from an elevated temperature shaping process and then artificially aged |
| T6 T651 |
Solution heat-treated and then artificially aged Solution heat-treated, stress relived by stretching a controlled amount (permanent set 1% to 3% for rolled or cold-finished rod and bar) and then artificially aged |
| T66 | Solution heat-treated and then artificially aged-mechanical property level higher than T6 achieved through special control of the process 6000 series alloys |
| T6511 | Solution heated-treaded, stress-relieved by stretching a controlled amount (permanent set 1% to 3% for extruded rod, bar, shapes and tube, 0.5% to 3% for drawn tube) and then artificially aged. Minor straightening is allowed after stretching to comply with standard tolerances |
Available Size Range
| Dimension | Range |
| Diameter | 6.0~350mm for Bar 101.6~406.4mm for Billet |
| Length | 1,000~6,000mm for Bar 500~5,800mm for Billet |
Application
Aluminum alloy round bar and aluminum alloy billet are widely applied in machinery, heat sink, heat exchanger, electronic appliances and components, vehicle, vessel parts, refrigerate plate, military, building material and raw material for extrusion.
– Production Process: Extruded, Cold Drawn
– Form & Image: Round
– Surface Finish: Mill Finish, unless otherwise specified
– Surface Protection: Paper interleaved for Bar, Naked for Billet